MC1300 PC/ABS (polycarbonate + acrylonitrile butadiene styrene copolymer) PC/ABS MC1300 is an injection molded PC/ABS blend with excellent flow and impact properties.
It is designed for electroplating applications with a specific gravity of 1.10g/cm ³, melt flow rate (melt flow rate) (260 °C kg 5.0 kg) 14g/10 min, mainly used in the automotive industry.
Its characteristics.
Combines the advantages of PC and ABS.
Impact resistance is good.
Can be electroplated.
Good liquidity.
Its application is mainly in the field of automobiles.
Its processing method is injection molding.
Its advantages are:
High impact strength, chemical stability, good electrical properties, high impact resistance, high heat resistance, flame retardant, reinforcement, high thermal deformation temperature, and good electroplating.
Good flexibility.
The mixed material also shows excellent flow characteristics.
The shrinkage is about 0.5%.
Dimensional stability, this high modulus resin product line is a series of amorphous filled PC/ABS mixtures that provide excellent dimensional stability in flame retardant and non-flame retardant products.
Its application field.
Dashboards, posts, instrument front cover printers, plotters, monitors,
Household switches, plugs, sockets, etc.
The flame retardant resin product line is a range of amorphous PC/ABS blends suitable for injection molding, extrusion, and thermoforming applications.
The improvement of toughness is based on the great advantage of standard LEXAN resins, this series of high-impact resins have higher impact properties and low-temperature ductility.
Typical application range:
Computer and business machine housings, electrical equipment, lawn and gardening machines, auto parts dashboards, interior decoration, and wheel covers.
Injection mold.
Process conditions:
Drying treatment: drying treatment before processing is necessary.
The humidity should be less than 0.04%, and the recommended drying condition is 90cm 110C for 2h.
Melting temperature: 230m 300c.
Mold temperature: 50mm 100C.
Injection pressure:
It depends on the plastic parts.
Injection speed: as high as possible.
Chemical and physical properties: PCIABS has the comprehensive characteristics of both PC and ABS.
For example, the easy processing of ABS and the excellent mechanical properties and thermal stability of PC.
The ratio of the two will affect the thermal stability of PCIABS materials.
The mixed material PCIABS also shows excellent flow characteristics.
The shrinkage is about 0.5%.
PC/ABS MC1300 basic innovative plastic is a kind of modified engineering plastic synthesized by mixing.
Among them, PC is polycarbonate and ABS is the copolymer of acrylonitrile (A), butadiene (B), and styrene (S).
This modified plastic has better properties than simple PC and ABS, such as improved impact resistance, heat resistance, hardness, and so on.
Other features:
The main results are as follows: 1. Good comprehensive properties, high impact strength, chemical stability, and good electrical properties.
It has good weldability with 372 plexiglass and can be made into two-color plastic parts, which can be coated with chromium and spray paint.
High impact resistance, high heat resistance, flame retardant, reinforcement, transparency, and other grades.
Increase the heat stability of ABS, improve the low temperature of the PC, the impact resistance of the back wall, and reduce the cost.
It is widely used in typewriter shells, word processors, computer equipment shells, medical equipment components, small household appliance components, electronic equipment components, car headlamp frames, taillight covers, food plates, and so on.
Liquidity is a little worse than HIPS, better than PMMA, PC, etc., and more flexible.